Laporkan Masalah

PENYAMBUNGAN BAJA ST60 MENGGUNAKAN METODE FRICTION WELDING

IRAWAN, Widia Setiawan,ST., MT.

2014 | Tugas Akhir | D3 TEKNIK MESIN

Disektor manufaktur ditemukan banyak komponen yang membutuhkan metode pengelasan yang efektif dan efisien. Sehingga proses pengelasan harus dengan biaya yang rendah untuk melakukan pengelasan beberapa material, seperti penyambungan poros dengan poros. Kemudian proses pengelasan yang dapat diaplikasikan adalah friction welding. Oleh karena itu, friction welding diperlukan penelitian untuk menyambung baja ST60. Dari material lasan dapat ditemukan sifat mekanik dan fisik setelah melewati beberapa pengujian. Material baja ST60 yang digunakan dalam penelitian. Material ini disambungkan menggunakan mesin bubut, spindle harus diputar dengan kecepatan 1100 rpm hingga permukaan material saling bergesekan dan menyambung. Spesimen melewati uji metalografi, uji kekerasan dan uji kekuatan tarik. Uji metalografi dilakukan untuk mengenali struktur mikro dan uji kekerasan dilakukan untuk memperoleh distribusi kekerasan pada logam induk, daerah HAZ dan logam sambungan. Analisa terhadap nilai kekerasan pada tiga daerah yaitu, logam induk, HAZ, dan logam sambungan akan terkait dengan perubahan struktur mikro. Tetapi peningkatan temperatur mengakibatkan nilai upset menjadi lebih lebar dan logam menjadi lebih pendek. Metode friction welding dapat diaplikasikan untuk penyambungan baja ST60. Struktur mikro pada sambungan ditemukan perubahan ukuran, itu artinya friction welding merubah sifat mekanik. Kekerasan logam lasan menjadi meningkat dari 205 VHN hingga 233 VHN. Dan kemudian untuk kekuatan tarik menjadi meningkat dari rata-rata 6 spesimen yaitu 75,208 kg/mm2.

In manufacturing sector was found much component needed effective and efficient of welding method. So that welding process had to with lower cost for carry out joined some materials, such as joined shaft with shaft. Then welding process which could apply was friction welding. Therefore it was needed the research to joint the solid ST60. From material welded could find mechanical and physic properties after pass through several testing. Material ST60 was used in research. This material was joined used lathe machine, the spindle must rotation 1100 rpm in velocity up to the material surface become friction and joined. The specimen was through test for metallographic, hardness test and tensile test. The metallography test was done recognize the microstructure and the hardness test was conducted to obtain the hardness distribution in the base metal, in the HAZ region, and in the welding metal. Analyses for the value of hardness in the three region namely, base metal, HAZ, and welding metal will be related to the change in microstructure. But the increase the temperature effection the upset value become larger and the sample become shorter. Friction welding method can applied for the joint solid steel ST60. The microstructure in the joining was found size change that mean there is change in mechanical properties. The hardness of welding metal become increase from 205 VHN until 233 VHN. And then for tensile strength become increase from six specimen averages are 75,208 kg/mm2.

Kata Kunci : Las Gesek, Sifat mekanik dan fisik, Baja ST60


    Tidak tersedia file untuk ditampilkan ke publik.