Penelitian ini bertujuan untuk mempelajari pengaruh temperatur tuang, temperatur cetakan, tekanan dan ketebalan coran terhadap sifat fisis dan mekanis pada pengecoran squeeze (direct squeeze casting) pada paduan Al–6,4%Si–1,93%Fe. Paduan dilebur pada dapur krusibel dan dituang pada variasi temperatur 650°C, 700°C dan 750°C, pada cetakan yang berbentuk die-punch yang dipanaskan pada variasi temperatur 300°C, 400°C dan 500°C. Tekanan diberikan pada cetakan sebesar 0 MPa, 50 MPa, 75 MPa dan 100 MPa selama 100 detik untuk mendapatkan variasi ketebalan coran 10 mm, 35 mm dan 70 mm. Perubahan struktur mikro diamati dengan menggunakan mikroskop optik, perubahan sifat mekanis dilakukan dengan pengujian kekerasan Brinell dan pengujian tarik. Hasil pengujian menunjukkan bahwa pengecoran squeeze mampu mengurangi penyusutan dan porositas, struktur silikon semakin halus, SDAS semakin kecil, meningkatkan dan meratakan distribusi kekerasan Brinell serta menaikkan tegangan tarik maksimum. Pada pengecoran squeeze, peningkatan temperatur tuang tidak berpengaruh secara signifikan terhadap struktur mikro dan kekerasan. Peningkatan temperatur cetakan menyebabkan struktur silikon semakin kasar, kekerasan dan kekuatan tarik turun.

The objective of this research is to study the effect of pouring temperature, die temperature, pressure and thickness of direct squeeze casting on physical and mechanical properties of Al–6,4%Si–1,93%Fe alloy. Alloy was melted on crucible furnace and pour into the die with variety temperature namely 650, 700, and 750°C. The die had been preheated before on temperature variations of namely 300, 400 and 500°C. During the solidification process, the melt was pressured with 0, 50, 75 and 100 MPa for 100 second. The alloy was cast in 10, 35 and 70 mm of casting thickness. Optical microscope was used to observe the microstructure of alloy. The hardness and tensile strength was measured in order to find the mechanical properties. Direct squeeze casting can eliminate shrinkage and porosity, refine silicon structure, make SDAS smaller, also increase Brinell Hardness Number and tensile strength. The increase of pouring temperature is not significant to modify microstructure and increase hardness. The decreasing die temperature causes the refinement of microstructure, increase of hardness and tensile strength.

Kata Kunci : Sifat Fisis dan Mekanis,Pengecoran Squeeze,Tebal Coran, squeeze casting, thickness cast, physical and mechanical properties